HH800 Curtain Wall Structural Adhesive
Model No.: HH 800
Brand: HH
Place of Origin：China
Wet: 750g/pieces
Payment Type：LC,T/T
Incoterm：FOB,CFR,CIF,EXW
Min Order：30 pieces
Port: Qingdao,Shanghai,Tianjin
1.Introduction of products
HH800 is a single-component, ultra-high strength, neutral curing silicone structural adhesive designed specifically for structural assembly in curtain wall systems. It is mainly used for glass, ceramic, glass fiber, non-oily wood, aluminum profile and paint material surface. Powder sprayed aluminum alloy must be completely removed by solvent wax coating.
2.Product advantages
(1) high strength, high elongation, suitable for high-rise, super high-rise curtain wall, large plate glass curtain wall, aluminum curtain wall, steel structure main curtain wall and other buildings;
(2) neutral curing, non-corrosive to the sticky surface;
(3) excellent weather aging resistance, excellent high and low temperature resistance;
(4) for most of the building materials have excellent adhesion, generally do not need to use primer;
(5) with other silicone rubber has good compatibility.
3.Product parameters are as follows
Serial Number | Inspection Item | Qualification | Measured Value | Test Mode | ||
1 |
Droop | Vertical Placement，mm | ≤3 | 0 |
GB/T 13477 | |
Horizontal Placement | No Deformation | No Deformation | ||||
2 | Extrusion Sex，s | ≤10 | 4.2 | GB/T 13477 | ||
3 | Table Dry Time，h | ≤3 | 0.3 | GB/T 13477 | ||
4 | Application Period, at 20min，s | ≤10 | / | GB/T 13477 | ||
5 | Shore Hardness，Shore A | 20～60 | 47 | GB/T 531.1 | ||
6 |
Heating Ageing | Hot Weightlessness，% | ≤10 | 3.2 |
GB 16776 | |
Chap | NO | NO | ||||
Chalking | NO | NO | ||||
7 |
Stretching Bonding |
Stretch Bond Strength， MPa | 23℃ | ≥0.60 | 1.36 |
GB/T 13477 |
90℃ | ≥0.45 | 0.95 | ||||
-30℃ | ≥0.45 | 1.99 | ||||
After Soaking Water | ≥0.45 | 1.42 | ||||
Water-UV Light Exposure Behind |
≥0.45 |
1.23 | ||||
Adhesion Damage Area，% | ≤5 | 0 | ||||
at Maximum Tensile Strength at 23℃ Long Rate，% |
≥100 |
286 | ||||